著者：Chao-Ching Chang; Feng-Hsi Huang; Liao-Ping Cheng

著錄名稱、卷期、頁數：Pigment & Resin Technology 48 (1), p.36-44

摘要：Purpose The purpose of this paper is to investigate the effects of dipentaerythritol hexaacrylate (DPHA) and 3-(trimethoxysilyl)propyl methacrylate-modified silica nanoparticles (MSiO2) contents on the performances of the Disperse Red 1 (DR1)-grafted-silica/poly(acrylate) color hard coatings. Design/methodology/approach The organic dye DR1 was silylated by reaction with the coupling agent 3-isocyanatopropyltriethoxysilane in methyl ethyl ketone. The silylated-DR1 thus obtained was grafted on MSiO2 to form dye-grafted silica (GSiO2). This hybrid dye was then UV-cured with the cross-linking agent, DPHA, to yield color coatings. Thermal durability of the coatings was evaluated based on their CIE (international commission on illumination) chromaticity coordinates and UV/Vis transmittances. Findings The results indicated that GSiO2-coatings could tolerate thermal attack better than pristine DR1-coatings or dye-absorbed silica (DSiO2)-coatings because of the fact that DR1 was more finely dispersed in the polymer binder when covalently bonded to the silica particles. Under optimal conditions, coatings with very small change of saturation and hue after high-temperature treatments were obtainable. These coatings appeared transparent, had 3H-6H pencil hardness and adhered perfectly onto the poly(methyl methacrylate) substrates. Practical implications Dye-grafted color coatings may find applications such as color filter photoresists for displays, microelectronics, printed circuit boards, etc. Originality/value The performances of the coatings were evaluated in terms of mechanical strength, adherence to the substrate, transmittance and color stability against heat treatments, which have not been disclosed. Also, using a newly developed triangular composition diagram, suitable ranges for preparing useful color coatings were accessed. The present method deserves further research studies on green and blue dyes.

關鍵字：Dyes;Thermal stability;Resins;Coloured callus;Nanocomposite coatings;Pencil hardness;Silica nanoparticles

語言：en

期刊性質：國外

收錄於：SCI EI

審稿制度：是

國別：GBR

出版型式：電子版,紙本